Thin films of the elusive intermediate uranium oxide U2O5 have been prepared by exposing UO3 precursor multilayers to atomic hydrogen. Electron photoemission spectra measured about the uranium 4f core-level doublet contain sharp satellites separated by 7.9(1) eV from the 4f main lines, whilst satellites characteristics of the U(IV) and U(VI) oxidation states, expected respectively at 6.9(1) and 9.7(1) eV from the main 4f lines, are absent. This shows that uranium ions in the films are in a pure pentavalent oxidation state, in contrast to previous investigations of binary oxides claiming that U(V) occurs only as a metastable intermediate state coexisting with U(IV) and U(VI) species. The ratio between the 5f valence band and 4f core-level uranium photoemission intensities decreases by about 50% from UO2 to U2O5, which is consistent with the 5f 2 (UO2) and 5f 1 (U2O5) electronic configurations of the initial state. Our studies conclusively establish the stability of uranium pentoxide.
Pubmed ID: 29844333
Publication data is provided by the National Library of Medicine ® and PubMed ®. Data is retrieved from PubMed ® on a weekly schedule. For terms and conditions see the National Library of Medicine Terms and Conditions.
A complete graphing and data analysis software package that provides a suite of features catering to the needs of scientists and engineers. Main features: * Drag-and-drop import of data and images * Save import settings to a worksheet or external files for repeated use * Use saved settings to re-import files with a single click * Post-process imported data * Import Wizard with visual feedback * Handle non-standard files by programming
View all literature mentions